Case-Hardened 20CrMnTi KR Series Stud Type Track Rollers are dimensioned to DIN 5429 / ISO 1206 exactly as the standard version is: the material changes the properties, never the envelope. What it does change — none of its own; protected in service exactly as through-hardened bearing steel is, magnetic and the service range similar to through-hardened rings — about +120 °C without special stabilization — is set out below with the full size chart.
Why Case-Hardened 20CrMnTi for KR Series Stud Type Track Rollers
Chosen for shock loading and for heavy ring sections, where a tough core resists the cracking a fully through-hardened section would not survive. In a kr series stud type track rollers it is the steel of the rings and, in most designs, of the rolling elements.
Carburizing puts the hardness where the rolling contact is and leaves the core tough, so the ring can absorb shock and heavy section stresses that would crack a through-hardened ring. It is the usual choice for large roller bearing rings and for anything that gets hit rather than merely loaded.
Material Properties
| Grade designation | 20CrMnTi (GB/T 3077), of the same class as 20MnCr5 and SAE 8620 — carburized to a hard case over a tough, unhardened core |
|---|---|
| Magnetic response | Magnetic |
| Service temperature | Similar to through-hardened rings — about +120 °C without special stabilization |
| Corrosion characteristic | None of its own; protected in service exactly as through-hardened bearing steel is |
Service Limits
The case has a depth, and that depth is a design limit: load high enough and the maximum shear stress moves below the hardened case into the softer core, where the surface then collapses. That is why case depth is specified against the rolling element size and the load, and why a case-hardened ring is not simply a tougher version of a through-hardened one.
What the Material Changes About the Bearing
The material does not change the envelope: the bore, the outside diameter, the width and the corner radius stay exactly as the boundary dimension standard fixes them, so the bearing is interchangeable with any other bearing of the same designation. What it changes is what happens inside the contact — the fatigue behavior, the tolerance of shock, and the temperature at which the ring stops being dimensionally stable.
Sizes of KR Series Stud Type Track Rollers Available in Case-Hardened 20CrMnTi
| Designation | Stud thread | Roller outer diameter D (mm) | Roller width C (mm) | Stud diameter (mm) |
|---|---|---|---|---|
| KR16 | M6 | 16 | 11 | 6 |
| KR19 | M8 | 19 | 11 | 8 |
| KR22 | M10 | 22 | 12 | 10 |
| KR26 | M10 | 26 | 12 | 10 |
| KR30 | M12 | 30 | 14 | 12 |
| KR32 | M12 | 32 | 14 | 12 |
| KR35 | M16 | 35 | 18 | 16 |
| KR40 | M16 | 40 | 18 | 16 |
| KR47 | M20 | 47 | 24 | 20 |
| KR52 | M20 | 52 | 24 | 20 |