Material specification page for 32200 series tapered roller bearings in Case-Hardened 20CrMnTi. Covers the grade designation (20CrMnTi (GB/T 3077), of the same class as 20MnCr5 and SAE 8620 — carburized to a hard case over a tough, unhardened core), what the material does inside the bearing, its temperature and environmental limits, the alternatives worth considering, and the sizes available to ISO 355 / DIN ISO 355 / GB/T 297.
Why Case-Hardened 20CrMnTi for 32200 Series Tapered Roller Bearings
Chosen for shock loading and for heavy ring sections, where a tough core resists the cracking a fully through-hardened section would not survive. In a 32200 series tapered roller bearings it is the steel of the rings and, in most designs, of the rolling elements.
Carburizing puts the hardness where the rolling contact is and leaves the core tough, so the ring can absorb shock and heavy section stresses that would crack a through-hardened ring. It is the usual choice for large roller bearing rings and for anything that gets hit rather than merely loaded.
Material Properties
| Grade designation | 20CrMnTi (GB/T 3077), of the same class as 20MnCr5 and SAE 8620 — carburized to a hard case over a tough, unhardened core |
|---|---|
| Magnetic response | Magnetic |
| Service temperature | Similar to through-hardened rings — about +120 °C without special stabilization |
| Corrosion characteristic | None of its own; protected in service exactly as through-hardened bearing steel is |
Service Limits
The case has a depth, and that depth is a design limit: load high enough and the maximum shear stress moves below the hardened case into the softer core, where the surface then collapses. That is why case depth is specified against the rolling element size and the load, and why a case-hardened ring is not simply a tougher version of a through-hardened one.
Alternatives and When to Switch
Through-hardened GCr15 is the alternative and the default: it is used wherever the section is modest and the load is steady, which is most of the catalog. Case-hardened rings earn their place under shock and in large sections.
Fitting a Steel Bearing in an Aluminum Housing
Aluminum has roughly twice the coefficient of thermal expansion of bearing steel, so a housing bore machined to a normal H7 fit at room temperature grows away from the outer ring as the machine reaches operating temperature. The outer ring then turns in its seat and wears the bore. Where the housing is aluminum and the temperature rise is more than about 30 degrees C, tighten the housing fit by one grade — J7 or K7 in place of H7 — or fit a steel sleeve into the aluminum. Check the resulting internal clearance: a tighter housing fit takes clearance out of the bearing, which is often why C3 is specified alongside it.
Sizes of 32200 Series Tapered Roller Bearings Available in Case-Hardened 20CrMnTi
| Designation | Bore d (mm) | Outer diameter D (mm) | Assembled width T (mm) | Width B (mm) | Width C (mm) | Contact angle a (deg) | Chamfer r min (mm) |
|---|---|---|---|---|---|---|---|
| 32204 | 20 | 47 | 19.25 | 18 | 15 | 12.95 | 1 |
| 32205 | 25 | 52 | 19.25 | 18 | 16 | 14.04 | 1 |
| 32206 | 30 | 62 | 21.25 | 20 | 17 | 14.04 | 1 |
| 32207 | 35 | 72 | 24.25 | 23 | 19 | 14.04 | 1.5 |
| 32208 | 40 | 80 | 24.75 | 23 | 19 | 14.04 | 1.5 |
| 32209 | 45 | 85 | 24.75 | 23 | 19 | 15.11 | 1.5 |
| 32210 | 50 | 90 | 24.75 | 23 | 19 | 15.64 | 1.5 |
| 32211 | 55 | 100 | 26.75 | 25 | 21 | 15.11 | 2 |
| 32212 | 60 | 110 | 29.75 | 28 | 24 | 15.11 | 2 |
| 32213 | 65 | 120 | 32.75 | 31 | 27 | 15.11 | 2 |
| 32214 | 70 | 125 | 33.25 | 31 | 27 | 15.11 | 2 |
| 32215 | 75 | 130 | 33.25 | 31 | 27 | 16.17 | 2 |
| 32216 | 80 | 140 | 35.25 | 33 | 28 | 15.64 | 2.5 |
| 32217 | 85 | 150 | 38.5 | 36 | 30 | 15.64 | 2.5 |
| 32218 | 90 | 160 | 42.5 | 40 | 34 | 15.64 | 2.5 |
| 32219 | 95 | 170 | 45.5 | 43 | 37 | 15.64 | 3 |
| 32220 | 100 | 180 | 49 | 46 | 39 | 15.64 | 3 |