HK Series Drawn Cup Needle Roller Bearings are needle roller bearings manufactured to ISO 3245 / DIN 618-1 / GB/T 290. This page carries the complete boundary-dimension table — bore, outer diameter, width and corner radius for every designation in the series — with the materials, mounting and selection notes that go with it.
What Are HK Series Drawn Cup Needle Roller Bearings?
HK Series Drawn Cup Needle Roller Bearings are needle roller bearings defined by ISO 3245 / DIN 618-1 / GB/T 290. They are selected by bearing designation and the dimensional characteristics shown below. Material, cage and sealing are specified separately from the designation and are covered further down this page.
Materials & Cage
Drawn cups are case-hardened low-carbon steel, formed and then carburized, and they run directly on the shaft — so the SHAFT is a bearing raceway and must be hardened to 58 to 64 HRC and ground to h5 or h6. Machined rings and needles are through-hardened GCr15 / 100Cr6. Where the shaft cannot be hardened, specify a variant with an inner ring instead.
Typical Applications
Planet gears, universal joints, connecting rods, pumps and automotive transmissions, where the radial section available for the bearing is the limiting dimension. Read the full application guide for HK Series Drawn Cup Needle Roller Bearings →
Pricing
HK Series Drawn Cup Needle Roller Bearings are supplied to order. Pricing starts from approximately US$0.60 per piece for standard sizes in case-hardened steel, without an inner ring; final pricing depends on size, material, finish and order quantity (MOQ applies). Submit your exact configuration with the quote form above.
Specifying the HK Series Drawn Cup Needle Roller Bearings
The sizes specified most often from this range are 6 mm bore, 8 mm bore, 10 mm bore and 12 mm bore. Each has its own page, so a drawing can be checked against one bore without reading the whole table above.
Where the environment decides the specification rather than the load, the material pages are the ones to read: GCr15 Bearing Steel, Case-Hardened 20CrMnTi and Pressed Steel Cage. Each states what the grade survives, and what choosing it costs in load capacity or temperature range.
For the machines and duties this type is actually specified for, see where hk series drawn cup needle roller bearings are fitted.
Manufactured in our own plant
This bearing is forged, hardened, ground, superfinished and clearance-set in-house. The stages below are where its tolerance class, its internal clearance and its noise grade are actually decided.
-
01 Forging & turning
GCr15 bar and tube is cut, heated and forged into ring blanks, then turned to leave a uniform grinding allowance. Forging rather than machining from solid keeps the grain flow following the raceway, which is the surface that eventually fails.
Blank dimensions and grinding stock checked at set-up and per shift.
-
02 Heat treatment
Through-hardening brings GCr15 / 100Cr6 to 58–64 HRC; carburizing case-hardens 20CrMnTi where the section is heavy or the load is shock. Rings are then stabilized so they hold size in service rather than growing in the housing.
Core and surface hardness per lot; retained austenite and dimensional stability to the ordered temperature class.
-
03 Raceway grinding
Faces, bore, outer diameter and raceway are ground in sequence on separate machines. This is where the tolerance class is created: P0, P6, P5 or P4 is a grinding outcome, not a sorting outcome.
Bore and outer diameter deviation, raceway roundness and face runout measured to ISO 492 on every setup.
-
04 Honing & superfinishing
The ground raceway is honed to remove the grinding lay and bring surface roughness down to a fraction of a micrometre. Raceway finish is what decides whether a lubricant film forms, and therefore what decides bearing life far more than the load rating alone.
Surface roughness Ra and waviness measured per lot.